Keo dán polymer MS đa năng có độ bền cao cho việc dán gỗ

High strength 1-Component MS Polymer Adhesive

High strength MS Polymer adhesive

MS137

MS137 is a high quality one-component adhesive based on MS Polymer technology. It has high adhesive strength and initial tack performance.

It has excellent adhesion to glass fiber reinforced plastic, XPS foam board, powder coating sheet metal parts, metal, wood, plastic and other materials with good adhesion properties.

Suitable for high strength sealing or bonding in construction, automotive, marine, and industrial applications. It works on various substrates like plastic, metal, rubber, natural materials (wood, polywood, leather, cloths, paperboard etc.) & inorganics (concrete, mortar, natural stone, tile, glass, porcelain etc.).

SPECIAL CHARACTERISTICS

• Eco-friendly, odorless;

• High modulus, high strength;

• Solvent free- No shrinkage

• Isocyanate-free - No air bubbling

• Primerless bonding to most substrates

• High ageing and weathering resistant.

APPLICATION EXAMPLES

• Used in vehicle, elevator and machinery industry;

Bonding and sealing of metal, plastic, wood, glass, ceramics and other materials. Meets hygiene requirements for ventilation and air-conditioning systems

Specification Data Sheet

Items Standard Specification Typical value

Appearance Visual Uniform paste Black / white / gray

uniform paste

Density (g/cm3) GB/T 13477 1.5 ± 0.1 1.48

Sagging (mm) GB/T 13477 < 1 0

Tack free time (min) GB/T 13477 10 ~ 20 10

Curing speed (mm/d) HG/T 4363 ≥ 3.5 4.0

Solid content (%) GB/T 2793 ≥ 97 99

Hardness (Shore A) GB/T 531 50 ± 5 45

Tensile strength (MPa) GB/T 528 ≥ 2.5 3

Elongation at break (%) GB/T 528 ≥ 300 350

Shear strength (MPa)

3003 Alu -3003 Alu GB/T 7124 ≥ 2.0 2.2

Shear strength

FRP - FRP (MPa) GB/T 7124 ≥ 2.0 2.2

Service temperature ( ºC) / -40 ~ +90 /